AWS E312-16 Stainless Steel Welding Electrode Rod
Solder / Filler Rod is a kind of dual-phase steel electrode with lime-titania type coating.Due to the 40% ferrite in the deposited metal, solder has excellent crack resistance. Solder has excellent welding performance. The filler rod is used for welding high-carbon steel, tool steel, high temperature steel, armor steel, dissimilar steel, etc. The soldering rod has excellent welding performance, excellent crack-resistance, and dual-phase steel electrode with lime-titania type coating.
Model Number: E312-16 stainless steel electrode
Material: Stainless Steel
Length: 300mm-500mm
Diameter: 2.0mm,2.5mm,3.2mm,4.0mm
Application: High strength ash iron and ball mill iron welding
| Dual-phase Stainless Steel Electrode AWS E312-16 GB E312-16 | |
|
Introduction: A1002 is a kind of dual-phase steel electrode with lime-titania type coating. Due to the 40% ferrite in the deposited metal, it has excellent crack-resistance. It has excellent welding performance. |
|
|
Uses: Used for welding high-carbon steel, tool steel, high temperature steel, armor steel, dissimilar steel, etc. |
Chemical Composition of Deposited Metal (%)
| Chemical Composition | C | Mn | Si | S | P | Ni | Cr |
| Guarantee Value | ≤0.15 | 0.5~2.5 | ≤0.90 | ≤0.030 | ≤0.040 | 8.0~10.5 | 28.0~32.0 |
Mechanical Properties of Deposited Metal
| Test Item | Rm(MPa) | A(%) |
| Guarantee Value | ≥660 | ≥22 |
Reference Current (AC, DC+)
| Electrode Diameter(mm) | φ2.5 | φ3.2 | φ4.0 | φ5.0 |
| Welding Current (A) | 50~80 | 80~110 | 110~160 | 160~220 |
Instructions:
1.The electrodes should be baked under about 250°C for an hour before welding.
2.Direct current had better be used and the current should not be too strong.