AWS A5.23: ECF3 Submerged Arc Cored Wires Low-Alloy Steel
DESCRIPTION:
AWS A5.23: ECF3 is a low-alloy composite metal-cored wire electrode for submerged arc welding in high strength applications. And it meets AWS A5.23 chemistry F3, and is designed for tensile strength levels above 100 ksi.
FEATURES&BENEFITS:
Metal-cored wire can offer improved deposition rates compared to solid wires at comparable amperages
Metal-cored wires offer broader penetration profiles compared to solid wires at comparable welding parameters
Weld deposit chemical composition requirements are identical to those of EF3 solid wires
Weld deposit chemical composition consists of less than 1% nickel
Very good low-temperature impact toughness in both the as-welded and stress-relieved conditions
Provides potential to increase travel speed for improved productivity
Helps to prevent burn-through when welding at high currents on root passes and relatively thin materials.
Suitable as a higher-productivity alternative in many applications currently using EF3 solid wire
Suitable for use in sour gas applications where stress corrosion cracking due to hydrogen-sulfide is a concern
Helps minimize the risk of cracking in critical applications and harsh service environments
INDUSTRIES:
Structural fabrication, oil &gas, power generation, heavy equipment
WIRE TYPE:
Metal-powder, metal-cored wire
CURRENT:
HN-590, SWX 120, SWX 150
CURRENTD:
irect Current Electrode Positive (DCEP), Direct Current Electrode Negative (DCEN), Alternating Current (AC)
STORAGE:
Product should be stored in a dry, enclosed environment, and in its original intact packaging
AWS CLASSIFICATIONS:
TYPICAL MECHANICAL PROPERTIES:
TYPICAL OPERATING PARAMETERS:
Maintaining a proper welding procedure - including pre-heat and interpass temperatures - may be critical depending on the type and thickness of steel being welded.
Parameters are provided for informational purposes only. All values are approximate. The optimal voltage may vary (typically ±2 volts) depending on the choice of flux, material thickness, joint design, and other variables specific to the application.
Likewise, actual deposition rate may vary depending on choice of flux and contact tip to work distance.